當(dāng)雙組份膠在混合過(guò)程中就發(fā)生局部固化時(shí)，膠槍打出來(lái)的膠就會(huì)出現(xiàn)結(jié)皮或硫化現(xiàn)象。雙組份打膠機(jī)在這里提示大家，出現(xiàn)這一現(xiàn)象的原因主要有三種：
When local curing occurs in the mixing process of two-component rubber, crust or vulcanization will occur in the rubber produced by rubber gun. There are three main reasons for this phenomenon:
⑴膠體顏色較黑，固化快時(shí)，可能是由于B組分比例過(guò)高，過(guò)多的催化劑促使固化速度加快。此時(shí)，需要適當(dāng)降低B組分的比例，將結(jié)皮或硫化膠沖洗干凈后施工；
(1) When the colloid is black and solidified quickly, it may be due to the high proportion of B component, and the excessive catalyst promotes the speed of solidification. At this time, it is necessary to reduce the proportion of B component appropriately and rinse the crust or vulcanizate before construction.
⑵若打膠過(guò)程中伴有出膠慢的現(xiàn)象時(shí)，可能是混合芯長(zhǎng)時(shí)間未清洗或清洗不徹底，膠體結(jié)皮堵塞管道。因此，定期清洗靜態(tài)混合器是很有必要的。
(2) If the gelling process is accompanied by slow gelling, it may be that the mixed core has not been cleaned for a long time or is not thoroughly cleaned, and the gel crust blockages the pipeline. Therefore, it is necessary to clean the static mixer regularly.

⑶當(dāng)固化和出膠速度均無(wú)異常，而打出的膠仍有結(jié)皮或硫化現(xiàn)象時(shí)，則可能是設(shè)備停機(jī)時(shí)間較長(zhǎng)，膠槍未清洗或洗槍不夠徹底，需要將結(jié)皮或硫化膠沖洗干凈后后施工。
(3) When there is no abnormal curing and tapping speed, and there is still crust or vulcanization in the tapped rubber, it may be that the equipment has been shut down for a long time, the rubber gun has not been cleaned or the gun has not been cleaned thoroughly enough, so it is necessary to rinse the crust or vulcanizate before construction.
本文的精彩內(nèi)容由雙組份打膠機(jī)的小編提供知識(shí)，本網(wǎng)站還有很多的精彩內(nèi)容，更多的內(nèi)容您可以點(diǎn)擊進(jìn)入：http://linshi.jncsjx.com我們的客服為您耐心的解答問(wèn)題，歡迎前來(lái)咨詢！
The wonderful content of this article is provided by the small edition of the two-component glue machine. There are many wonderful contents on this website. You can click on more content to enter: http://linshi.jncsjx.com. Our customer service will patiently answer your questions. Welcome to consult!